Carbon Nanotube Masterbatches CNT-PP-20 (cod 070105)

 

nanotubi in pellet 

Specifiche

Carbon Nanotube Masterbatches CNT-PP-20

Our carbon nanotube masterbatches CNT-PP-20 use our industrial grade multi walled carbon nanotubes. This product has a 20% CNTs loading ratio.

The CNT-PP-20 material can be used with 3D printers, molders, & extruders.  Once received, you simply let it down and run it in your equipment.  Sold by the kilogram

Product Code

Matrix Resin

Matrix Resin Loading

CNTs Code

CNTs Loading

CNT-PP-20

Homopolymer PP

80wt%

IGMWNTs

20wt%

PP was diluted by PP 300 using twin-screw extruder, then the specimens were made by compression molding. Volume and surface resistivity were measured by high insulation resistance instrument ZC-90D（IEC 60093-1980, the test voltage is 100V）.

CNTs Loading（wt%）

1.5

2

Volume Resistivity (ohm.cm)

>1014

3.3×106

Surface Resistivity (ohm)

1.6×1013

2.2×106

 PP was diluted by PP SP179 (copolymer, izod notched impact strength is about 40~45 KJ/m2) using twin-screw extruder, then the specimens were made by injection molding. The standard of mechanical property of specimens was ISO 527, ISO 180 and ISO 178.

CNTs Loading（wt%）

0
（PP300 50%,
SP179 50%）

6
（PP300 44%,
SP179 50%）

8
（PP300 42%,
SP179 50%）

10
（PP300 40%,
SP179 50%）

Tensile Strength（MPa）

28.1

30

31.2

30.2

Stain at break（%）

49.4

36.9

43.6

41.4

Izod Notched Impact Strength（KJ/m2）

9.2

18.4

33.4

47.3

Flexural Strength（MPa）

33.7

34.5

34.2

33.4

Flexural Modulus（MPa）

1139

1266

1254

1196

Melt Index
（g/10min，
2.16Kg/230℃）

12.3

2.2

1.92

1.77

 

Approfitta delle proprietà dei nanotubi di carbonio miscelati con polipropilene per le tue applicazioni. Masterbatches Carbon Nanotube CNT-PP-20 è una soluzione pronta per l'uso che non richiede la dispersione dei nanotubi di carbonio e la miscelazione con il polipropilene.

0,12 €/grammo iva escl.     Quantità (g)  minimo 1Kg